Glare surface school chemical lab Island bench solid anti high temperature manufacturer from China ShangHai Weizhen Industrial CO.,LTD

Glare surface school chemical lab Island bench solid anti high temperature

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Glare surface matte surface laboratory bench top for chemical engineering

Glare surface matte surface laboratory bench top for chemical engineering

Description :

All of our laboratory bench tops are monolithic epoxy materials, there are molded marine edge to stop spill chemicals. The common color is black, we can also customize color according to client’s need.
The laboratory bench top total thickness is 32mm, actually it is 19+13mm, the thickness of dished area is 19mm, the thickness of marine edge is 13mm.
Advantages of laboratory bench top is easy to install and clean. Of course, it has perfect properties on resisting chemicals and heat.

Specification:

No.	Test Item	Test Method	Result
1	Flexural Strength	ASTM D790-10 Method A	12200psi
1	Flexural Modulus	ASTM D790-10 Method A	2350000psi
2	Density	ASTM D792-13 Method B	133.8lb/ft3
3	Rockwell Hardness	ASTM D785-08 Procudure A	HRM98.3

Advantages :

Repairability : All of our products are monolithic epoxy resin, if there are some scratches on the surface, it can repaired with the sand paper polishing.
Heat Resistance : ONUS’s worktop can resist 262 , it won’t foam and crack, the fire can extinguish because it has no any of paper materials.
Mositure Resistance : Due to our products are monolithic, it won’t swell and distortion on the mositure area.

Physical Test :

Rockwell Hardness : HRM98.3
Deflection Temperature Under Load : 262
Fire Resistance Test : No bubbles, rupture, crack on the surface

Application:

Epoxy resin worktops are use in all kinds of laboratories. In view of the rigid request for laboratory, epoxy resin worktops are vey popular in laboratory industry, it is the best choice for lab staff. The laboratory include the following: